The surface features of activated stibnite surface with copper or lead ion
,
 
,
 
,
 
 
 
More details
Hide details
1
State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization, Kunming, 650093, Yunnan, PR China
 
2
Faculty of Land Resources Engineering, Kunming University of Science and Technology, Kunming 650093, Yunnan, PR China
 
3
Faculty of Information Engineering and Automation, Kunming University of Science and Technology, Kunming, 650093, Yunnan, PR China
 
 
Corresponding author
Qinbo Cao   

Kunming University of Science and Technology, Faculty of Land Resources Engineering, Kunming University of Science and Technology, 650093 kunming, China
 
 
Physicochem. Probl. Miner. Process. 2018;54(3):763-770
 
KEYWORDS
TOPICS
ABSTRACT
Cu2+ and Pb2+ are widely used as activators for the flotation of stibnite. In this work, by the treatment of Cu2+ or Pb2+, the activation product and the thickness of activation layer on the stibnite surface were both investigated. Based on the flotation results, zeta potential analysis and X-ray photoelectron spectroscopy (XPS) study, it was found that Cu2+ was reduced to Cu+ at the stibnite surface and a layer of Cu2S was formed at the surface. While, a PbS layer presenting at the stibnite surface is responsible for the activation flotation of stibnite with Pb2+. Time of flight secondary ion mass spectrometry (TOF-SIMS) analysis further implies that, when stibnite was activated with 5×10-5 mol/dm3 of CuSO4 or Pb(NO3)2, the thickness of Cu2S layer on the Cu-activated surface was close to 2.7 nm, while the thickness of PbS layer was about 1.8 nm on the Pb-activated surface.
 
REFERENCES (21)
1.
ADAMS, M., LAWRENCE, R., BRATTY, M., (2008), Biogenic sulphide for cyanide recycle and copper recovery in gold–copper ore processing, Minerals Engineering, 21, 509-517.
 
2.
ALBERICI, S.G., ZONCA, R., PASHMOKOV, B., (2004), Ti diffusion in chalcogenides: a ToF-SIMS depth profile characterization approach, Applied Surface Science, 231, 821-825.
 
3.
ANDERSON, C.G., (2012), The metallurgy of antimony, Chemie der Erde - Geochemistry, 72, 3-8.
 
4.
CHELGANI, S.C., HART, B., (2014), TOF-SIMS studies of surface chemistry of minerals subjected to flotation separation – A review, Minerals Engineering, 57, 1-11.
 
5.
CHELGNI, S.C., HART, B., XIA, L., (2013), A TOF-SIMS surface chemical analytical study of rare earth element minerals from micro-flotation tests products, Minerals Engineering, 45, 32-40.
 
6.
DAI, Y.H., WANG, Q.L., ZHOU, H.Q., (2009), Process Study on some Antimony Ore in Xinning of Hunan Province, Hunan Nonferrous Metals, 25, 16-18.
 
7.
HUANG, K., (1987), The flotation behavior and surface electrical property of antimonite, J. Cent.-South Inst. Min. Metall.(China), 1, 105-109.
 
8.
JIANG, Y., YU, B.B., LIU, J., LI, Z.H., SUN, J.K., ZHONG, X., HU, J., SONG, W.G., WAN, L.J., (2015), Boosting the Open Circuit Voltage and Fill Factor of QDSSCs using Hierarchically Assembled ITO@Cu2S Nanowire Array Counter Electrodes, Nano Letters, 15, 3088-3095.
 
9.
KHMELEVA, T.N., BEATTIE, D.A., GEORGIEV, T.V., SKINNER, W.M., (2013), Surface study of the effect of sulphite ions on copper-activated pyrite pre-treated with xanthate, Minerals Engineering, 16, 601-608.
 
10.
LAGER, T., FORSSBERG, K.S.E., (1989), Beneficiation characteristics of antimony minerals a review- part 1, Minerals Engineering, 2, 321-336.
 
11.
LAGER, T., FORSSBERG, K.S.E., (2015), Comparative study of the flotation properties of jamesonite and stibnite, Scandinavian Journal of Metallurgy, 18, 122-130.
 
12.
LI, H., MU, S., WENG, X., ZHAO, Y., SONG, S., (2016), Rutile flotation with Pb2+ ions as activator: Adsorption of Pb2+ at rutile/water interface, Colloids and Surfaces A: Physicochemical and Engineering Aspects ,506, 431-437.
 
13.
MAO, D., BLATZ, G., JR, C.E.W., GLOECKLER, M, (2016), Correlative impurity distribution analysis in cadmium telluride (CdTe) thin-film solar cells by ToF-SIMS 2D imaging, Solar Energy Materials & Solar Cells, 157, 65-73.
 
14.
PENG, Y., GRANO, S., (2010), Effect of grinding media on the activation of pyrite flotation, Minerals Engineering, 23, 600-605.
 
15.
SARVARAMINI, A., LARACHI, F., HART, B., (2016), Collector attachment to lead-activated sphalerite – Experiments and DFT study on pH and solvent effects, Applied Surface Science, 367, 459-472.
 
16.
SOLOZHENKIN, P.M., ZINCHENKO, Z., KRILOVA, I., IVANOVA, N., (1991), Flotation of complex antimony ore, Proceedings of the 17th international conference on mineral processing, Dresden, Germany, pp. 163-174.
 
17.
SUI, C.C., BRIENNE, S.H.R., XU, Z.H., FINCH J.A., (1997), Xanthate adsorption on Pb contaminated pyrite, International Journal of Mineral Processing, 49, 207-221.
 
18.
THOMAS, J.P., ZHAO, L., ABDELLAH, M., HEINIG, N.F., LEUNG, K.T., (2013), Interfacial micropore defect formation in PEDOT:PSS-Si hybrid solar cells probed by TOF-SIMS 3D chemical imaging, Analytical Chemistry, 85, 6840-6845.
 
19.
WANG, H., ZHOU, A., PENG, F., YU, H., YANG, J., (2007), Mechanism study on adsorption of acidified multiwalled carbon nanotubes to Pb(II), Journal of Colloid & Interface Science, 316, 277-283.
 
20.
XU, X., LIU, J.A., HU, X., (1991), Non-chromate flotation separation of complex stibntie-cinnaber ore, Nonferrous Metals, 1, 25-32.
 
21.
ZWIERNIK, M.J., QUENSEN, J.F., BOYD, S.A., (1998), FeSO4 Amendments Stimulate Extensive Anaerobic PCB Dechlorination, Environmental Science & Technology, 32, 3360-3365.
 