The article presents the results of studying the effects of technological parameters of milling upon surface roughness and microhardness of C45 steel objects after laser cutting. The metallographic structure formed as an effect of cutting by laser was also analyzed. The milling was performed on a FV-580a vertical machining centre. Depth of cut and feed per tooth were changed within the following range: ap = 0.09–0.18 mm and fz = 0.02–0.17 mm/tooth. To measure the surface roughness a Surtronic 3+ profile graphometer was used, whereas microhardness was measured with the use of a Leco LM 700AT microhardness tester. The surface roughness was significantly improved as a result of milling. The laser beam input and output zones were eliminated. Only a part of the layer hardened by laser cutting was removed while milling, in effect of which after milling the hardness of surface layer is much higher than hardness of the core.